micro-XRCT data set of Carrara marble with artificially created crack network: fast cooling down from 600°C
DaRUS
2020
doi:10.18419/darus-682/1doi:10.18419/darus-682/2
micro-XRCT data set (projection and reconstructed images) of a Carrara marble core with a diameter of 5 mm. The sample was extracted with a water-cooled diamond drill from a bigger sample with a diameter of 30 mm and a length of 80 mm which was before subjected to following thermal treatment to initiate cracks: Starting at room temperature (20°C) the sample was heated up with a rate of 3 K/min to 600°C. After a holding time of 2 hours at this temperature, the sample was subsequently quenched in water at room temperature (20°C).
Steeb, Holger(University of Stuttgart, Institute of Applied Mechanics (CE) & SimTech)University of Stuttgart, Institute of Applied Mechanics (CE) - Chair for Continuum-MechanicsUniversity of Stuttgart - SC SimTech